Product Details:
|
| Grade: | 301/304/316/430 | Thickess: | 0.05-3mm |
|---|---|---|---|
| Width: | 10-2000mm | Hardness: | Full Hard 1/2H 3/4H |
| Coil Id: | 508/610mm | Technical: | Cold Rolled |
| Samples: | Free To Supply | Advantage: | High Strengthen |
| Specification: | Cold Rolled Or Hot Rolled | Finish: | 2B,NO.4,BA,HL |
| Technical Treatment: | Code Rolled Hot Rolled | Processing Service: | Cutting |
| Form: | Coils, Strip Etc. | Hs Code: | 72193500 |
| Highlight: | stainless steel coil stock,cold rolled stainless steel coil |
||
| Chemical Composition Limits | |||||||||
| Weight% | C | Si | Mn | P + S max | Cr | Ni | Cu | Mo | Fe |
| AMS 5518 301 1/2 Hard |
0.15 max | 1.00 max | 2.0 max | 0.040 P 0.030 S |
16-18 | 6-8 | 0.75 max | 0.75 max | Bal |
Grade 301 is a 17% Chromium / 7% Nickel austenitic stainless steel. It is supplied in a range of different conditions/tempers depending on the level of strength required. It has good resistance to atmosphere corrosion and its bright attractive surface make it an excellent choice for decorative structural applications.
Resistance to Corrosion & Oxidation
Grade 301 has good resistance to oxidation at temperatures up to 1550°F, but is not recommend for use above 1600°F. 301 is resistance to a variety of corrosive media. However, it's corrosion resistance properties are not as good as the 18-8 chromium-nickel steels and its susceptibility to carbide precipitation during welding restricts its use in many applications in favour of 304/304L alloy. The mechanical properties for the different tempers of 301 are obtained by cold working and not by heat treating. 301 1/2 Hard (AMS 5518) material has a miniumum tensile strength of 150ksi and is used in the fabrication of parts that require strength and involves moderate drawing or forming.
| Condition | Tensile Strength Min | 0.2% Yield Strength Min | Elongation % in 2" (50.8mm) | Hardness HRC | ||
| Ksi | MPa | Ksi | MPa | |||
| AMS 5901 301 Annealed |
75 | 515 | 30 | 205 | 40 | 92 HRB |
| AMS 5517 301 1/4 Hard |
125 | 862 | 75 | 517 | 25 | 25 |
| AMS 5518 301 1/2 Hard |
150 | 1,034 | 110 | 758 | 18 | 32 |
| AMS 5902 301 3/4 Hard |
175 | 1,207 | 125 | 931 | 12 | 37 |
| AMS 5519 301 Full Hard |
185 | 1,276 | 140 | 965 | 9 | 41 |
Availability
Availability: 301 1/2 Hard is available in sheet and strip. View stock list for further information (Foil Stock List, Sheet Stock List, Plate Stock List.) for all availability contact Sales.
Related Specifications
AMS 5901 301 Annealed Stainless Steel sheet and strip, cold rolled, 75ksi min (MIL-S-5059)
AMS 5517 301 1/4 Hard Stainless Steel sheet and strip, cold rolled, 125ksi min (MIL-S-5059)
AMS 5902 301 3/4 Hard Stainless Steel sheet and strip, cold rolled, 175ksi min (MIL-S-5059)
AMS 5519 301 Full Hard Stainless Steel sheet and strip, cold rolled, 185ksi min (MIL-S-5059)
UNS S30100
AISI 301 Stainless Steel Strip Full Hard DIN1.4310 Strip in Coil 1.25mm*1400mmT.S 900Mpa Min
ASTM A240 for annealed condition
ASTM A666 for tempered material*
Kitchenware
Pots, Pans, Flatware, Counters, Sinks, Appliance components
Automotive
Trim, Moldings, Wiper parts, Fastener parts
Appliance
Dishwashers, Ovens, Refrigerators
Hardware
Hinges, Doors, Frames, Roll formed sections, Spring clips, Clamps
Food processing
Various equipment including conveyor belts
Structural parts
Aircraft, Trailer bodies, Rapid transit cars, Cargo containers
| Composition per ASTM A240 | |
| Carbon | .15 Max |
| Manganese | 2.00 Max |
| Phosphorus | .045 Max |
| Sulfur | .030 Max |
| Silicon | 1.00 Max |
| Chromium | 16.00 – 18.00 |
| Nickel | 6.00 – 8.00 |
| Nitrogen | .10 Max |
| Molybdenum | |
| Mechanical Properties (Annealed, Per ASTM A240) | |
| UTS | 75,000 ksi Min |
| Elongation % in 2″ | 40.00 Min |
| Rockwell Hardness | RB95.00 Max |
* Tempered mechanical properties are available upon request.
301 stainless steel flat rolled coil is non-magnetic in the annealed condition but becomes magnetic when cold worked.
Type 301 is used in fabrication by bending, roll forming, blanking, stretch bending and drawing. It’s high work hardening rate helps minimize wall thinning when deformed. Deep drawing may require intermediate annealing or higher nickel content.